Our UNS SS400 Mild Steel Hr Plate is been sourced from the highest quality steel manufacturers in the world and it is have been evaluated and assessed by our procurement team.
Mild Steel SS400 Plates is popular for proper tensile strength and toughness, good plasticity, welding performance and processing property. It is always supplied in hot rolled condition.
The chemical composition of SS400 MS Plates consists of phosphorous 0.050max,
sulphur 0.050%max, It is widely used for numerous industries and applications and due to its excellent performance and quality it is as considered among the best steel grade.
MS DIN St37-2 Hot Rolled Plates is for general applications. It is more reliable compared to SS330 for its tensile strength. It is the most commonly used hot rolled general structural steel.
Mild STEEL SS400 High Quality Plates isunder JIS3101 standard, we can regard as Carbon and low alloy steel SS400 steel plate is mainly due to Carbon and low alloy steel, MS SS400 High Quality Plates would be used to build containers which can bear low temperature sea water.
MS SS400 Plate mechanical properties consist of Density: 7860kg/m3, Young’s Modulus: 190-210GPa, Tensile Strength: 400 – 510 MPa, Yield Strength: 205-245 MPa, Poisson’s ratio: 0.26 and Hardness Brinell Hardness: 160HB
Mild Steel Ss400 Cr Plates is a kind of steel for general structure, and it is used in ship, house, bridge making and so on. This kind of steel plate sheet SS400 has some features like its heat condition, excellent freezing, even structure with pressure resistance and its good mechanical properties.
SS400 Mild Steel Cr Plates covers carbon structural steel shapes, plates, and bars of structural quality for use in riveted, bolted, or welded construction of bridges and buildings, and for general structural purposes.
ASTM MS SS400 Chequered Plate heat analysis shall be used to determine the required chemical compositions of carbon, manganese, silicon, phosphorus, sulphur, and copper. Tensile strength, yield strength, and elongation shall be evaluated by using tension test and must conform to the required tensile properties.
| Type | Description | USA FOB Price | Malaysia FOB Price | Europe FOB Price | Singapore FOB Price | Saudi Arabia (KSA) FOB Price | |||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Unit Per mtr | Unit Per mtr | Unit Per mtr | Unit Per mtr | Unit Per mtr | |||||||
| ss400 Plates | Size : 10mm x 2000 x 6000 | US $ | 2.78 | Malaysia Ringgit | 11.31 | Euro | 2.34 | Singapore Dollar | 3.73 | Saudi Riyal | 10.43 |
ASTM A36 SS400 Mild Steel Plate
Q235 SS400 Hot Rolled Sheet
S235JR SS400 Hr Plate
SS400 JIS G3101 MS Plates
Mild Steel Ss400 Sheet
Ms Din St37-2 Hot Rolled Plates
| Grade | Fe | Si | C | S | P | |
| SS400 | min. | 99.25 | – | – | – | – |
| max. | 100 | 0.4 | 0.26 | 0.050 | 0.040 | |
| Grade | Yield Strength min. (Mpa) |
Tensile Strength (Mpa) |
Elongation min. % | ImpactResistancemin.[J] | |||
| Thickness ＜16 mm |
Thickness ≥16mm |
Thickness | Thickness | Thickness | |||
| ＜5mm | 5-16mm | ≥16mm | |||||
| SS400 | 245 | 235 | 400-510 | 21 | 17 | 21 | – |
| SS400 Equivalent Steel Grade | |||||||||||||
| Japan | US | European Union | ISO | China | Canada | India | |||||||
| Standard | Steel | Standard | Grade | Standard | Steel | Standard | Grade | Standard | Steel | Standard | Grade (SI) | Standard | Grade |
| JIS G3101 | SS400 | ASTM A36 | A36 steel | EN 10025-2 | S235 (S235JR) | ISO 630 | S235 | GB/T 700 | Q235 | CSA G40.21 | 44W (300W) | IS 2062 | E250 |
| Density and specific gravity, g/cm3 | 7.85 |
| melting point, ℃ | 1494-1527 |
| Specific heat capacity, J/(Kg·K) | 473 at 20 ℃ |
| Electrical resistivity, μΩ·m | About 0,15 (20 ℃) |
| Long. elastic modulus, GPa | 206 |
| Tr. modulus of elasticity, GPa | 79 |
| Shear modulus, GPa | 79 |
| Thermal conductivity, (W/m·K) | 57-60 |
| Linear expansion coefficient, (10-6/K) | 11.3-11.6 (20 ℃) |
| Young’s modulus, GPa | 206 |
| Poisson’s ratio | 0.3 |
| Magnetic permeability, mm2/s | 13.9 |
| SS400 Steel Plate Thickness in mm. | ||||||||
| 1.2 | 1.4 | 1.6 | 1.8 | 2.0 | 2.3 | 2.5 | (2.6) | 2.8 |
| (2.9) | 3.2 | 3.6 | 4.0 | 4.5 | 5.0 | 5.6 | 6.0 | 6.3 |
| 7.0 | 8.0 | 9.0 | 10.0 | 11.0 | 12.0 | 12.7 | 13.0 | 14.0 |
| 15.0 | 16.0 | (17.0) | 18.0 | 19.0 | 20.0 | 22.0 | 25.0 | 25.4 |
| 28.0 | (30.0) | 32.0 | 36.0 | 38.0 | 40.0 | 45.0 | 50.0 | |
| Material thickness tolerance in mm | ||||||
| Thickness (t) | Steel Plate width (W)<1600 | 1600≤ W <2000 | 2000≤ W <2500 | 2500≤ W <3150 | 3150≤ W <4000 | 4000≤ W <5000 |
| 4.00≤t<5.00 | ±0.45 | ±0.55 | ±0.55 | ±0.65 | – | – |
| 5.00≤t<6.30 | ±0.50 | ±0.60 | ±0.60 | ±0.75 | ±0.75 | ±0.85 |
| 6.30≤t<10.00 | ±0.55 | ±0.65 | ±0.65 | ±0.80 | ±0.80 | ±0.90 |
| 10.00≤t<16.00 | ±0.55 | ±0.65 | ±0.65 | ±0.80 | ±0.80 | ±1.00 |
| 16.00≤t<25.00 | ±0.65 | ±0.75 | ±0.75 | ±0.95 | ±0.95 | ±1.10 |
| 25.00≤t<40.00 | ±0.70 | ±0.80 | ±0.80 | ±1.00 | ±1.00 | ±1.20 |
| 40.00≤t<63.00 | ±0.80 | ±0.95 | ±0.95 | ±1.10 | ±1.10 | ±1.30 |
| 63.00≤t<100.00 | ±0.90 | ±1.10 | ±1.10 | ±1.30 | ±1.30 | ±1.50 |
| 100.00≤t<160.00 | ±1.30 | ±1.50 | ±1.50 | ±1.70 | ±1.70 | ±1.90 |
| 160.00≤t<200.00 | ±1.60 | ±1.80 | ±1.80 | ±1.90 | ±1.90 | ±2.10 |
| 200.00≤t<250.00 | ±1.80 | ±1.90 | ±1.90 | ±2.00 | ±2.00 | ±2.20 |
| 250.00≤t<300.00 | ±2.00 | ±2.10 | ±2.10 | ±2.20 | ±2.20 | ±2.50 |
| 300.00≤t≤350.00 | ±2.10 | ±2.30 | ±2.30 | ±2.40 | ±2.40 | ±2.80 |
| Standard width of steel plate and steel belt (mm) | |||||||||
| 600 | 630 | 670 | 710 | 750 | 800 | 850 | 900 | 914 | 950 |
| 1000 | 1060 | 1100 | 1120 | 1180 | 1200 | 1219 | 1250 | 1300 | 1320 |
| 1400 | 1500 | 1524 | 1600 | 1700 | 1800 | 1829 | 1900 | 2000 | 2100 |
| 2134 | 2438 | 2500 | 2600 | 2800 | 3000 | 3048 | |||